Titanium Grade 23
90% Ti, 6% V, 4% Others,Highly Biocompatible Type IV

Non-Precious Cobalt Chrome

66% Co, 27% Mo, 6% Others,Unique 255 Vick. Hardness
Alloys
Gold Crown & Bridge Noble
SM20 – 20% Au, Type IV
Gold Crown and Bridge High Noble
SM55 – 55% Au, Type IV
Ceramic – PFM Noble
Phoenix PXN 76% PD,Type IV For Porcelain Application
Ceramic – PFM High Noble
SMOG 77% Au, Type IV 
For Porcelain Application
Titanium Grade 23
90% Ti, 6% V, 4% Others,Highly Biocompatible Type IV
Non-Precious Cobalt Chrome
66% Co, 27% Mo, 6% Others,Unique 255 Vick. Hardness

ALLOYS

Ceramic - Non Precious

66% Co, 27% Mo, 6% Others, Unique 255 Vick. Hardness

SMCoCr is a clinically proven cobalt-based ceramic alloy demonstrating outstanding properties.
Advantages
  • Clinically proven
  • Extra hard 
  • Wide range of indications 
  • Certified biocompatibility
Indications
  • Onlays 
  • Inlays 
  • Partial crowns
  • Single crowns
  • Telescope and conus crowns 
  • Short-and long-span bridges 
  • Implant superstructures
Composition
  Co 66
Cr 27
Mo 6
Si < 1.0, Mn < 1.0
Technical data
Type
4
Color
White
Density (g/cm³)
8.4
Melting range (°C)
1307 – 1417
Melting point (°C)
1467
Modulus of Elasticity (GPa)
233
CTE (25 – 500 °C) 14.3 x 10-6 K-1
14.3
Elongation (%)
11.0
Vickers hardness (HV10)
255
Maximum load strength (MPa)
678

Handling Instructions

Print this Section

Lightly sandblast the entire surface of the framework upon receipt. This step is intended to simply create a clean surface to begin working with.

ONLY AREAS REQUIRING ADJUSTING NEED FINISHING.

Perform finishing with dedicated burs or non-contaminating stones. ALL OTHER SURFACES CAN SIMPLY BE SANDBLASTED. IT IS NOT NECESSARY TO PERFORM TRADITIONAL METAL FINISHING ACROSS THE ENTIRE SURFACE.

When finishing steps are completed, sandblast the surface using non-recycled 110µ TO 150µ AL2O3 at max. 36 to 43 PSI or 2.5 / 3 bar pressure then clean in ultrasonic or with steam.

Oxidation

Oxidize at 950°C – 980°C for 5 minutes under vacuum. Oxidation high temperature is 10° higher than your opaque cycle high temp.

Opaque

Do not use a bonder. Ideal opaque coverage may require three applications. Follow this with standard body and incisal porcelain application and glazing per your porcelain kit instructions.